6082 Aluminum Plate

Share to:

6082 aluminum plate

GRADE: 6000 SERIES  

TEMPER: O,T4,T5, T6, T651, F

THICKNESS: 1-600MM

WIDTH: UNDER 2650MM

STANDARD: GB/T, ASTM, EN, DIN

Availability:

6082 Aluminum Plate


Alloy 6082 is typically supplied as plate and sheet. 

it is an aluminum primarily alloyed with silicon and manganese. 

The addition of manganese controls the grain structure which in turn results in a stronger alloy. 

The most common tempers for 6082 aluminum are O, T4, T6 and T651 and 6082 is slightly higher mechanical properties in the T6 condition when bending or forming. 

6082 aluminum plate also corresponds to DIN 3.2315, EN AW-6082 and AA6082 standard designations and specifications but may not be a direct equivalent.


6082 Aluminum Plate



chemical   composition (%)


Si

Fe

Cu

Mn

Mg

Cr


6082

0.7-1.3

0-0.5

0.1

0.4-1.0

0.6-1.2

0.25











Physical   specificatiom


Density
  (kg/m3)

σ0.2/MPa

σb/MPa

δ/%




6082 T6

-

260

310

10





6082 Aluminum Plate


Our packing meets the sea export standard. 

PE/PVC protective film or white paper could be covered as customer’s need. 

Special requirements of packing could be negotiate before order.

aluminum plate package


6082 Aluminum Plate


Typical material properties for 6082 aluminum alloy include weld ability, bribability, solder ability se well as mach inability. 

Besides, alloy 6082 is a medium strength alloy with excellent corrosion resistance. 

So various commercial joining methods (welding, brazing, etc.) can be easily applied to 6082 alloy. 

Since 6082 is a heat treatable alloy, strength will be reduced in the weld region. 

6082 aluminum sheet and plate are typically formed by rolling. 

6082 aluminum plate and sheet for highly stressed applications includes trusses, bridges, cranes, transport applications as well as mould.

aluminum application